Macherey-Nagel GmbH
Cellulose Adsorbents for Column Chromatography
Features
-
Cellulose MN 100: native fibrous cellulose, standard grade,
average degree of polymerization 620–680, fiber length (85 %) 20–100 μm,
specific surface acc. to Blaine ~ 6500 cm2/g
residue on ignition < 10000 ppm, < 20 ppm Fe, < 5 ppm Cu, < 7 ppm P, dichloromethane extract < 0.20 %
-
Cellulose MN 2100: native fibrous cellulose, purified grade (washed with different eluents),
average degree of polymerization 620–680, fiber length (85 %) 20–75 μm,
specific surface acc. to Blaine ~ 5500 cm2/g
residue on ignition < 1000 ppm, < 2 ppm Fe, < 1 ppm Cu, < 2 ppm P, dichloromethane extract < 0.15 %
grade MN 2100ff is a defatted cellulose MN 2100 with a dichloromethane extract < 0.02 %
Cellulose MN 100: native fibrous cellulose, standard grade,
average degree of polymerization 620–680, fiber length (85 %) 20–100 μm,
specific surface acc. to Blaine ~ 6500 cm2/g
residue on ignition < 10000 ppm, < 20 ppm Fe, < 5 ppm Cu, < 7 ppm P, dichloromethane extract < 0.20 %
average degree of polymerization 620–680, fiber length (85 %) 20–100 μm,
specific surface acc. to Blaine ~ 6500 cm2/g
residue on ignition < 10000 ppm, < 20 ppm Fe, < 5 ppm Cu, < 7 ppm P, dichloromethane extract < 0.20 %
Cellulose MN 2100: native fibrous cellulose, purified grade (washed with different eluents),
average degree of polymerization 620–680, fiber length (85 %) 20–75 μm,
specific surface acc. to Blaine ~ 5500 cm2/g
residue on ignition < 1000 ppm, < 2 ppm Fe, < 1 ppm Cu, < 2 ppm P, dichloromethane extract < 0.15 %
grade MN 2100ff is a defatted cellulose MN 2100 with a dichloromethane extract < 0.02 %
average degree of polymerization 620–680, fiber length (85 %) 20–75 μm,
specific surface acc. to Blaine ~ 5500 cm2/g
residue on ignition < 1000 ppm, < 2 ppm Fe, < 1 ppm Cu, < 2 ppm P, dichloromethane extract < 0.15 %
grade MN 2100ff is a defatted cellulose MN 2100 with a dichloromethane extract < 0.02 %
Order Information
| Designation | Pack of 1 kg | Pack of 5 kg | Pack of 25 kg | |
| Cellulose MN 100 | 815050.1 | 815050.5 | 815050.25 | |
| Cellulose MN 2100 | 815060.1 | 815060.5 | 815060.25 | |
| Cellulose MN 2100ff (cellulose MN 2100 defatted) | 815070.1 | |||